InspectAPedia TM
Building & Environmental Inspection, Testing, Diagnosis, Repair, & Problem Prevention Advice Home
Conditioning
Inspection
Ventilate
Inspect/Test
Water
Septic
Directory of Professionals to Inspect or Test a Building
InspectAPedia TM Building & Environmental Inspection, Testing, Diagnosis, Repair, & Problem Prevention Advice |
||||||||||||||||||||||||||
| InspectAPedia Home |
| | Air Conditioning |
| | Electrical | | | Environment | | | Exteriors | | | Heating | | | Home Inspection |
| | Insulate Ventilate |
| | Interiors | | | Mold Inspect/Test |
| | Plumbing Water Septic |
| | Roofing | | | Structure | | | Contact Us |
| Directory of Professionals to Inspect or Test a Building |
||||||||||||||||||||||||||
|
ROOFING INSPECTION & REPAIR CERTIFICATIONS for ROOFING CONTRACTORS CHOOSING A ROOFING CONTRACTOR ASPHALT ROOF SHINGLES FIRE RETARDANT PLYWOOD ROOF INSPECTION SAFETY & LIMITS SLATE ROOF INSPECTION & REPAIR How to Inspect & Repair Types of Roofing Slate Slate Colors, Chemistry Slate Roof Aging and Durability Ribbon Slates Slate Roof Installation Quality Other factors in Condition Slate Roof Repair history Slate Roof Leaks Slate Holding actions How to Repair Slate Roofs Copper Tab Method Slate Hook Method SLATE ROOF PHOTO LIBRARY About The Authors Slate References Slate Sources, Repairs SLATE ROOF INSPECTION CLASS STANDARDS for ROOFING WARRANTIES for ROOF SHINGLES WORKMANSHIP & WIND DAMAGE More Information Home Air Conditioning InspectAPedia Bookstore Electrical Environment Exteriors Heating Home Inspection Insulate Ventilate Interiors Mold Inspect/Test Roofing Plumbing Water Septic Structure More Information Accuracy & Bias Pledge InspectAPedia TM Home & Site Map Contact Us |
Slate Roof Wear, Aging & Durability
|
|
|
|
We were warned by an experienced slate roofer and we have confirmed by field inspections of slate roofs that determination of slate condition other than by direct up-close inspection is highly unreliable. Slates may look fine from the ground, but be found soft and at end of life on close inspection. By direct inspection we mean looking at slates from a few inches, either from a ladder or some other point of view such as an attic window. We strongly advise inspectors not to walk on slate roofs. Risks include falling - very slippery, and extensive damage to the slates.
Trapasso, personal communication.
The photographs provided here show how soft roofing slates can become. These slates might, from a distance, look pretty good, but I was easily able to crush the slates with my fingers. I do not agree that we should call this "rotted roofing slate" as did Trapasso, but on seeing how soft and delaminated this slate can become, we can understand his loose use of that term.
Darker gray "Buckingham" slates from Virginia are considered a durable high-quality material which, properly maintained, can have a near indefinite life. Average life of these slates is 175 years.
The Old House Journal, April, 1983 p. 57
Vermont slate roofs, with proper maintenance, can last indefinitely.
The Old House Journal, April 1983, p.58, and Slate Roofs, National Slate Association, p. 71.
By other sources, Vermont slates have life expectancy of 100-200 years.
Steven Trapasso, personal communication. Also the Old House Journal April 1983 rates Vermont slates as having a 175 year life.
Such roofs should be maintained, not replaced. With proper maintenance such an asset may be continued for an indefinite period. Inspectors who do not know the composition and source of slates would not want to condemn, except in the worst of circumstances, a Vermont slate roof.
Typical life for Pennsylvania slate roofs is 40-50 years. These life expectancies are general experience with the material and do not consider installation or environmental factors which vary from one building to the next.
Earlier British experimentation on slate durability and composition emphasized that variations in the tendency of slates to absorb water may be the principal cause of deterioration seen by modern inspectors. Slates which are soft, delaminating, and thus are at or near end of their useful life may have been damaged by frost. "That sort of slate", said Dr. Watson, the bishop of Llandaff, "other circumstances being the same, is esteemed the best, which imbibes the least water; for the imbibed water not only increases the weight of the covering, but, in frosty weather, being converted into ice, it swells and shivers the slate." Watson continued to suggest that slates, being less porous than clay roofing tiles of the day, were more durable.
The New Practical Builder and Workman's Companion
Watson's opinion that slates are more durable than clay tiles is arguable as both materials are found with considerable variation in composition. Indeed unglazed clay absorbs more water (up to 10%) than slate (usually 1%) but tiles are not necessarily damaged by these freeze-thaw conditions. Watson's comments pertain to use of slate in Britain.
The extent of color change in Pennsylvania [and possibly other] slates often indicates the extent of deterioration. More white, more efflorescence probably means more deteriorated.
The rate of slate deterioration on roofs depends on the source quarry and the depth from which the slates were cut. These determine the density and composition of the slate. Site conditions, such as the roof pitch, exposure to sun, building moisture and ventilation and exposure to mechanical damage also affect slate life. It is interesting to note that several references indicate that slates actually harden after being quarried and exposed. We'd presume that observation pertains to the early or initial state of use of the slates, and we found no reference which claimed some chemical or molecular process of permanent or continuing hardening over life.
Deteriorating Pennsylvania slate shows a mottled appearance, with white faded patches resulting from exposure to sunlight and moisture. The white areas generally begin at the three exposed sides of a slate, growing towards the center of the slate as a function of time and exposure. The white visible in Pennsylvania slate is evidence of efflorescence - lime deposited on the slate surface. If the whole slate is white in color and scaling you should consider the slate to be at the end of its life. However as long as the slates are physically intact the roof is serviceable. If a roofer recommends tearing off the whole roof you should ask to be shown examples of failed slates.
Fading versus mottling: It is important for an inspector to distinguish between the mottled edges-in whitening (efflorescence) and fading. By contrast to the efflorescence process, fading slates generally fade monotonically across the slate rather than from edges in. Faded slates will not show an obvious whitish powder of surface deposited mineral salts as thick as that left by efflorescence. All slates will fade from weather exposure. Those which have only minimal color change are classed as "permanent" or "unfading". Those which change more markedly are classed as "weathering".
Monotonically means that the color change is even across the material rather than showing up as a splotch, or a ring of white around darker color, or in other variations. It's a nice word, not recommended for inspection reports.
We've heard several explanations for the mechanism by which Pennsylvania slates deteriorate, of which the most interesting was the opinion that lime in the slates in the presence of moisture reacts to break down organic components in the slate. For slates higher in carbon or carbonaceous materials this may be indeed the most accurate explanation. Pennsylvania "Black Bed" quarried slates were high in carbonaceous impurities and were recommended by the Slate Association only for temporary buildings or for chalkboards. By the 1920's this slate was recognized as not as durable; you'd not expect to find it surviving on a building in 1991.
The National Slate Association reference does not detail the mechanism of slate deterioration. It does point out that the slate roof on the Saxon Chapel at Stratford-on-Avon was built 1100 years ago - still in good condition.
By Mr. Trapasso's account the decomposition of Pennsylvania slate may be understood as a process similar to decomposition of wood. The lime which was in the slate, when the slate was mined, had not caused deterioration because the slates were protected from sunlight. When the slate is split, cut, punched for use, the lime is in an inactive or dormant state. Following application on a roof surface the slate material is exposed to ultraviolet rays (sunlight) and moisture. These components cause the lime to break down the organic materials in the slate (shale), making the slate increasingly porous and causing the white efflorescence. Lime and other mineral salts are dissolved and deposited on the surface of the slate when moisture evaporates.
Slate Roofs, National Slate Association, p.71-76.
Examining quantitative analysis of slates from nineteen quarries we observe that while oxides of silica (SIO2) and aluminum oxide (AL2O3) are the dominant components of slates, almost all have measurable levels of calcium oxide (CaO) and other carbonates and oxides. There are dramatically higher levels of these materials in Pennsylvania slates (3%) than in slates from Vermont (.3%-.7%). Clearly there is more material available to form calcium carbonates and efflorescence in the shorter lived materials.
Slate Roofs p. 73
Carbon, which would be broken down in the process described by Trapasso, occurs in slates from only a few quarries, and then in usually small amounts of less than 1%. This would seem to argue against the "slate rots" explanation of deterioration.
The brown color of some slate may be from oxidizing iron content in the slate which is following a similar reactive path. We did not find references to brown in Virginia slates.
The known chronological age of slates may be available from an owner or other documentation. As with all materials, experienced inspectors rate the apparent wear age of the roof, not the actual age.
snow box - this illustration remains to be inserted
This snow guard intended to keep snow from sliding off of the roof, avoiding gutter damage or avoiding falling snow at building entrances.
Use links just below or at the left of each of our other website pages to navigate this document or to view other topics at this website. Green links show where you are in our document or website.
ROOF INSPECTION SAFETY & LIMITS
SLATE ROOF INSPECTION & REPAIR
How to Inspect & Repair
Types of Roofing Slate
Slate Colors, Chemistry
Slate Roof Aging and Durability
Ribbon Slates
Slate Roof Installation Quality
Other factors in Condition
Slate Roof Repair history
Slate Roof Leaks
Slate Holding actions
How to Repair Slate Roofs
Copper Tab Method
Slate Hook Method
SLATE ROOF PHOTO LIBRARY
About The Authors
Slate References
Slate Sources, Repairs
SLATE ROOF INSPECTION CLASS
Alan Carson and Dan Friedman are ASHI Members, home inspectors, educators and writers in Toronto and Poughkeepsie respectively. Information in this article is taken from the references shown below, from inspection experience, from opinions shared at ASHI and other education seminars, from the authors' personal, limited experience repairing and rebuilding of slate roofs, and from very helpful Bill Markcrow and Doug Sheldon at Vermont Structural Slate Co. We also paraphrased from a presentation to NY Metro ASHI Members by Mr. Steven Trapasso in October, 1990. Mr. Trapasso has 40 years experience in working with slate, and has a clear love affair with the material, particularly when it comes from Vermont.
InspectAPedia TM Home & Site Map - Building Inspection, Diagnosis, & Repair, Environmental Inspection & Testing - Research Website
Home Inspection Construction Consulting Services & advice for home buyers
Contact Daniel Friedman for website content suggestions or for fee-paid consulting
07/17/2007 - www.inspect-ny.com/roof/SlateRoofsATJ4.htm - © 2006-1991 Copyright Daniel Friedman All Rights Reserved